Low Subthreshold Slope AlGaN/GaN MOS-HEMT with Spike-Annealed HfO2 Gate Dielectric

초록

AlGaN/GaN metal-oxide semiconductor high electron mobility transistors (MOS-HEMTs) with undoped ferroelectric HfO2 have been investigated. Annealing is often a critical step for improving the quality of as-deposited amorphous gate oxides. Thermal treatment of HfO2 gate dielectric, however, is known to degrade the oxide/nitride interface due to the formation of Ga-containing oxide. In this work, the undoped HfO2 gate dielectric was spike-annealed at 600 degrees C after the film was deposited by atomic layer deposition to improve the ferroelectricity without degrading the interface. As a result, the subthreshold slope of AlGaN/GaN MOS-HEMTs close to 60 mV/dec and on/off ratio>10(9) were achieved. These results suggest optimizing the HfO2/nitride interface can be a critical step towards a low-loss high-power switching device.